	Repeating chemical structure unit of ; Polycarbonate made from bisphenol A
Physical Properties
Density (ρ)	1.20–1.22 g/cm3
Abbe number (V)	34.0
Refractive index (n)	1.584–1.586
Flammability	V0-V2
Limiting oxygen index	25–27%
Water absorption – Equilibrium(ASTM)	0.16–0.35%
Water absorption – over 24 hours	0.1%
Radiation resistance	Fair
Ultraviolet (1-380nm) resistance	Fair
Mechanical Properties
Young's modulus (E)	2.0–2.4 GPa
Tensile strength (σt)	55–75 MPa
Compressive strength (σc)	>80 MPa
Elongation (ε) @ break	80–150%
Poisson's ratio (ν)	0.37
Hardness – Rockwell	M70
Izod impact strength	600–850 J/m
Notch test	20–35 kJ/m2
Abrasive resistance – ASTM D1044	10–15 mg/1000 cycles
Coefficient of friction (μ)	0.31
Speed of sound	2270 m/s
Thermal Properties
Melting temperature (Tm)	267°C*
Glass transition temperature(Tg)	150°C
Heat deflection temperature – 10 kN (Vicat B)	145°C
Heat deflection temperature – 0.45 MPa	140°C
Heat deflection temperature – 1.8 MPa	128–138°C
Upper working temperature	115–130°C
Lower working temperature	−40°C
Linear thermal expansion coefficient (α)	65–70 × 10−6/K
Specific heat capacity (c)	1.2–1.3 kJ/(kg·K)
Thermal conductivity (k) @ 23°C	0.19–0.22 W/(m·K)
Thermal diffusivity (a) @ 25°C	0.144 mm²/s
Electrical Properties
Dielectric constant (εr) @ 1 MHz	2.9
Permittivity (ε) @ 1 MHz	2.568 × 10−11 F/m
Relative permeability (μr) @ 1 MHz	0.866(2)
Permeability (μ) @ 1 MHz	1.089(2) μN/A2
Dielectric strength	15–67 kV/mm
Dissipation factor @ 1 MHz	0.01
Surface resistivity	1015 Ω/sq
Volume resistivity (ρ)	1012–1014 Ω·m
Chemical Resistance
Acids – concentrated	Poor
Acids – dilute	Good
Alcohols	Good
Alkalis	Good-Poor
Aromatic hydrocarbons	Poor
Greases & Oils	Good-fair
Halogenated Hydrocarbons	Good-poor
Halogens	Poor
Ketones	Poor
Gas permeation @ 20 °C
Nitrogen	10 – 25 cm3·mm/(m2·day·Bar)
Oxygen	70 – 130 cm3·mm/(m2·day·Bar)
Carbon dioxide	400 – 800 cm3·mm/(m2·day·Bar)
Water vapour	1–2 gram·mm/(m2·day) @ 85%–0% RH gradient)
Economic Properties
Price	2.6 – 2.8 €/kg

ചില പ്രത്യേകയിനം പ്ലാസ്റ്റിക്കുകളാണ് പോളികാർബണേറ്റുകൾ. ലെക്സാൻ, മാക്രോലോൺ, മാക്രോക്ലിയർ തുടങ്ങിയ വ്യാപാരനാമങ്ങളിൽ ആഗോളവിപണിയിൽ അറിയപ്പെടുന്ന ഇവ തെർമോപ്ലാസ്റ്റിക് പോളിമറുകളിലെ ഒരു പ്രത്യേക വിഭാഗമാണ്. രാസപരമായി കാർബണേറ്റു ഗ്രൂപ്പുകൾ (–O–(C=O)–O–) കൊളുത്തുകളായുളള ശൃംഖലയാണ് പോളികാർബണേറ്റ്.^[4]^[5] പല അഭിലഷണീയ ഗുണങ്ങളുമുളള പോളികാർബണേറ്റ് ഗാർഹിക സാങ്കേതിക മേഖലകളിൽ നാനാവിധത്തിൽ ഉപയോഗപ്പെടുന്നു.

രസതന്ത്രം

ബിസ് ഫീനോൾ എയും ഫോസ്ജീനുമായുളള രാസപ്രക്രിയയിലൂടെയാണ് പോളികാർബണേറ്റ് ഉണ്ടാക്കിയെടുക്കുന്നത്

വിഷവാതകമായ ഫോസ്ജീൻ ഒഴിവാക്കാനായി, സോളിഡ് സ്റ്റേറ്റ് പോളിമറൈസേഷൻ, ട്രാൻസ് എസ്റ്ററിഫിക്കേഷൻ^[5] എന്നീ ഹരിതമാർഗ്ഗങ്ങളും പരിഗണനയിലുണ്ട്.

സവിശേഷതകൾ

സുതാര്യത, ദൃഢത, താപസഹനശക്തി എന്നിവ കാരണം പോളികാർബണേറ്റ്, പ്ലാസ്റ്റിക്കുകളുടെ പട്ടികയിൽ മുൻപന്തിയിൽ നിൽക്കുന്നു. തിളച്ച വെളളത്തിൽ പോളികാർബണേറ്റ് ഉരുപ്പടികൾ സ്റ്റെറിലൈസ് ചെയ്യാവുന്നതാകയാൽ ഭക്ഷ്യമേഖലയിലും, ചികിത്സാരംഗത്തും ഗ്ലാസ്സിനു പകരമായി ഉപയോഗിക്കുന്നു. പക്ഷെ, ഒരു ന്യൂനത എളുപ്പത്തിൽ പോറലുകളേൽക്കുന്നു എന്നതാണ്. മറ്റൊന്ന് ശൃംഖലയിലെ ബെൻസീൻ ഘടകങ്ങൾ പ്രകാശരശ്മികളേറ്റ് രാസപരിണാമത്തിനു വിധേയമാകുകയും അതുകാരണം ഉരുപ്പടികൾക്ക് മഞ്ഞ നിറം വരികയും ചെയ്യും. ഇതു മറയ്ക്കാനാണ് നിറം നൽകുകയോ, പ്രാതിരോധശക്തിയുളള രാസപദാർത്ഥങ്ങൾ( Stabilizers) ചേർക്കുകയോ ആവാം. . ^[6] ,^[7]

ഇതും കാണുക

CR-39, allyl diglycol carbonate (ADC) used for eyeglasses
Organic electronics
Mobile phone accessories
Thermoplastic polyurethane
Vapor polishing

അവലംബം

↑ M. Parvin and J. G. Williams (1975). "The effect of temperature on the fracture of polycarbonate". Journal of Materials Science. 10 (11): 1883.
↑ J. Blumm, A. Lindemann (2003). "Characterization of the thermophysical properties of molten polymers and liquids using the flash technique". High Temperatures-High Pressures. 35/36 (6): 627.
↑ CES Edupack 2010, Polycarbonate (PC) specs sheet
↑ Christopher, W.F (1962)). Polycarbonate. Reinhold Publishing Corp,New York. {{cite book}}: Check date values in: |year= (help); Unknown parameter |coauthor= ignored (|author= suggested) (help)CS1 maint: year (link)
↑ ^5.0 ^5.1 Volker Serini "Polycarbonates" in Ullmann's Encyclopedia of Industrial Chemistry, Wiley-VCH, Weinheim, 2000
↑ "Weathering A practical approach" (PDF). Archived from the original (PDF) on 2016-03-07. Retrieved 2012-05-03.
↑ [http://alexandria.tue.nl/extra2/200911292.pdf Photodegradation and Stability of Bisphenol A Polycarbonate in Weathering Conditions]

ബാഹ്യ ലിങ്കുകൾ

[1] M. Parvin and J. G. Williams (1975). "The effect of temperature on the fracture of polycarbonate". Journal of Materials Science. 10 (11): 1883.

[2] J. Blumm, A. Lindemann (2003). "Characterization of the thermophysical properties of molten polymers and liquids using the flash technique". High Temperatures-High Pressures. 35/36 (6): 627.

[3] CES Edupack 2010, Polycarbonate (PC) specs sheet

[4] Christopher, W.F (1962)). Polycarbonate. Reinhold Publishing Corp,New York. {{cite book}}: Check date values in: |year= (help); Unknown parameter |coauthor= ignored (|author= suggested) (help)CS1 maint: year (link)

[Ullmann-5] 5.0 ^5.1 Volker Serini "Polycarbonates" in Ullmann's Encyclopedia of Industrial Chemistry, Wiley-VCH, Weinheim, 2000

[6] "Weathering A practical approach" (PDF). Archived from the original (PDF) on 2016-03-07. Retrieved 2012-05-03.

[7] [http://alexandria.tue.nl/extra2/200911292.pdf Photodegradation and Stability of Bisphenol A Polycarbonate in Weathering Conditions]

[4]

[5]

[1]

[2]

[3]

[6]

[7]

പോളികാർബണേറ്റ്
Repeating chemical structure unit of Polycarbonate made from bisphenol A
Physical Properties
Density (ρ)	1.20–1.22 g/cm³
Abbe number (V)	34.0
Refractive index (n)	1.584–1.586
Flammability	V0-V2
Limiting oxygen index	25–27%
Water absorption – Equilibrium (ASTM)	0.16–0.35%
Water absorption – over 24 hours	0.1%
Radiation resistance	Fair
Ultraviolet (1-380nm) resistance	Fair
Mechanical Properties
Young's modulus (E)	2.0–2.4 G Pa
Tensile strength (σ_t)	55–75 MPa
Compressive strength (σ_c)	>80 MPa
Elongation (ε) @ break	80–150%
Poisson's ratio (ν)	0.37
Hardness – Rockwell	M70
Izod impact strength	600–850 J/m
Notch test	20–35 kJ/m²
Abrasive resistance – ASTM D1044	10–15 m g/1000 cycles
Coefficient of friction (μ)	0.31
Speed of sound	2270 m/s
Thermal Properties
Melting temperature (T_m)	267°C*
Glass transition temperature(T_g)	150°C
Heat deflection temperature – 10 kN (Vicat B)	145°C
Heat deflection temperature – 0.45 MPa	140°C
Heat deflection temperature – 1.8 MPa	128–138°C
Upper working temperature	115–130°C
Lower working temperature	−40°C^[1]
Linear thermal expansion coefficient (α)	65–70 × 10⁻⁶/K
Specific heat capacity (c)	1.2–1.3 kJ/(kg·K)
Thermal conductivity (k) @ 23°C	0.19–0.22 W/(m·K)
Thermal diffusivity (a) @ 25°C	0.144 mm²/s ^[2]
Electrical Properties
Dielectric constant (ε_r) @ 1 MHz	2.9
Permittivity (ε) @ 1 MHz	2.568 × 10⁻¹¹ F/m
Relative permeability (μ_r) @ 1 MHz	0.866(2)
Permeability (μ) @ 1 MHz	1.089(2) μN/A²
Dielectric strength	15–67 kV/mm
Dissipation factor @ 1 MHz	0.01
Surface resistivity	10¹⁵ Ω/sq
Volume resistivity (ρ)	10¹²–10¹⁴ Ω·m
Chemical Resistance
Acids – concentrated	Poor
Acids – dilute	Good
Alcohols	Good
Alkalis	Good-Poor
Aromatic hydrocarbons	Poor
Greases & Oils	Good-fair
Halogenated Hydrocarbons	Good-poor
Halogens	Poor
Ketones	Poor
Gas permeation @ 20 °C
Nitrogen	10 – 25 cm³·mm/(m²·day·Bar)
Oxygen	70 – 130 cm³·mm/(m²·day·Bar)
Carbon dioxide	400 – 800 cm³·mm/(m²·day·Bar)
Water vapour	1–2 gram·mm/(m²·day) @ 85%–0% RH gradient)
Economic Properties
Price	2.6 – 2.8 €/kg^[3]